Industry News

How many degrees should the lead-free tin bars be set properly during use?

Views : 87
Update time : 2022-09-06 16:48:46
Generally speaking, we should set the appropriate degree during use. I believe that many technical experts will discuss this issue. The general temperature of lead-free solder bar welding is set to 280 plus or minus 10 degrees, because there is no preheating for manual dip soldering. , so the temperature setting is generally higher. The main components of the commonly used environmentally friendly tin bars are composed of 99.3% tin and 0.7% copper. They are solid, silver-white and odorless. For high-demand welding, widely used in wave furnace, hand dip furnace. The temperature of the environmental protection tin bar (peak temperature) is 270~300 ℃, and the lead solder bar depends on the lead content and the material of the components to be welded.
High temperature tin bar:
The liquidus temperature is higher than the melting point of the tin-lead eutectic (183 ℃) and can be kept without oxidation at a working temperature of over 450 ℃. The tin bar that can be soldered normally is called a high-temperature tin bar. High temperature tin bars are specially formulated additives added to tin-lead alloys, which can also play and oxidize at temperatures above 450 °C. The product is suitable for welding processes with high working temperature requirements. Such as: tin on the lead pins of the transformer, etc.
Low temperature tin bar:
For solders with a melting point lower than 183°C, different soldering processes can be provided, and solder alloys with different melting points can be provided.
High anti-oxidation solder bar:
At the soldering temperature below 300℃, the surface of the liquid energy solder is like a mirror surface, the wetting time is short, and the expansion rate is larger than that of ordinary solder. Due to the addition of anti-oxidation, the solder joints are bright and beautiful, and it is suitable for wave soldering and hot dip soldering of PCB.
Anti-oxidation high temperature solder bar:
Under the high temperature condition of 450℃, the surface of the solder can maintain a silver-white mirror state for a long time, and the amount of slag is only about 1/7 of that of ordinary solder. It is suitable for wave soldering and hot dip soldering, especially for the manufacture of various transformers. Tin enamel for self-dissolving enameled wire. The effect of low slag amount not only reduces bad solder joints, saves costs, but also reduces soldering maintenance opportunities.
Related News
Read More >>
What are the main problems that exist during the soldering process of lead-free tin bars? What are the main problems that exist during the soldering process of lead-free tin bars?
Aug .01.2023
Leadless tin strip is an energy-saving raw material that does not contain lead chemicals, also known as low-carbon and environmentally friendly welding wire. It has been successfully tested according to SGS and has no air pollution. There are several main problems that exist in the production process. Below, the solder paste manufacturer will explain:
What are the differences between tin wire and silver wire? What are the differences between tin wire and silver wire?
Jul .21.2023
Solder wire, Chinese name: Solder wire, Solder wire, Tin wire, Tin wire, English name: Solder wire, Solder wire is composed of two parts: tin alloy and flux, the alloy composition is divided into tin lead, tin copper, and other additives added evenly to the middle part of the tin alloy.
The scope of use of solder wire and solder bar The scope of use of solder wire and solder bar
Feb .09.2023
There are some things you don't know about the use of solder wire, solder bar, and the scope of use
Proper use of solder wire Proper use of solder wire
Feb .09.2023
Proper use of solder wire and commonly used auxiliary materials